Dual gate oxide structure in semiconductor device and method thereof

ABSTRACT

In the method of manufacturing a dual gate oxide layer of a semiconductor device, which has first and second active regions operating at mutually different voltages on a semiconductor substrate, the first and second active regions having a device isolation layer of STI (Shallow Trench Isolation) structure; the method of manufacturing the dual gate insulation layer includes, forming the device isolation layer so that an uppermost part thereof is positioned lower than an upper surface of the first and second active regions, before forming a gate insulation layer corresponding to each of the first and second active regions. Whereby, it is be effective till a portion of trench sidewall utilized as the active region, to increase a cell current of the active region and to prevent a stringer caused by a stepped coverage between the active region and a field region and a dent caused on a boundary face between the active region and the field region.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a divisional of U.S. patent application Ser. No.10/876,277, filed Jun. 23, 2004, now pending, which is claims priorityfrom Korean Patent Application No. 2003-0040714, filed on Jun. 23, 2003,the disclosure of which are incorporated herein in its entirety byreference.

FIELD OF THE INVENTION

This disclosure relates to a semiconductor device, and moreparticularly, to a method of forming a dual gate oxide having oxidelayers based on different thickness in different voltage regions.

PRIOR ART OF THE INVENTION

In a semiconductor memory device such as an SRAM etc., an operatingvoltage of a transistor constituting a memory cell and an operatingvoltage of transistor positioned within a peripheral logic circuit toaccess data of the memory cell are typically different from each other,thus a thickness of gate insulation layers, e.g., oxide layers, are alsodifferent. Further, in the field of power devices such as LDI (LCDDriver IC) products, a low voltage operation for driving a logic circuitand a high voltage operation for driving an LCD are all necessary in adriving device, thus a gate oxide layer should have a dual gatestructure and an employment for a shallow trench isolation (STI)structure based on a reduction of line width, which is also tending tobe used.

However, in applying a dual gate oxide to the STI structure usingmanufacturing processes of the prior art, an uppermost part of thedevice isolation layer is positioned higher than an upper surface ofactive region, which causes a stepped coverage therebetween. If thestepped coverage occurs, a portion of trench sidewall ca not be used asthe active region, and a stringer occurs due to the stepped coveragebetween the active region and the field region. This also causes arelatively severe dent on a boundary face between the active region andthe field region owing to a wet etching rate difference betweenmaterials of a field oxide layer formed in the STI and a thermal oxidelayer formed in the active region.

The dual gate oxide manufacturing process of the prior art will bedescribed referring to FIGS. 1 a through 1 f in order to thoroughlyunderstand the causes of the above-mentioned phenomena.

Referring to FIGS. 1 a to 1 f illustrating a process sequence, a methodof forming dual gate oxide according to the prior art will be describedin detail. Herewith, the process will be described with six steps forthe explanatory convenience. In the drawings, reference character Iindicates a low voltage (LV) region of a substrate as a first activeregion on which a thinned gate oxide will be formed, and referencecharacter II designates a high voltage (HV) region as a second activeregion on which a thick gate oxide will be formed.

In a first step, as shown in FIG. 1 a, a pad oxide layer 102 and anitride layer 104 are accumulated sequentially on a semiconductorsubstrate 100 to form a layer 105. Next, on the nitride layer 104, aphotoresist pattern 109 is formed which will expose a portion where atrench for defining the first active region I and the second activeregion II will be formed, and a portion where a trench for a deviceisolation of each active region will be formed.

In a second step, as shown in FIG. 1 b, the nitride layer 104, the padoxide layer 102 and the semiconductor substrate 100 are etchedsequentially by using the photoresist pattern 109 as an etch mask, toform a trench t1 for defining the first active region I and the secondactive region II on the semiconductor substrate 100, and to form atrench t2 for isolating devices on each active region. Then, theremaining photoresist pattern 109 is removed through an ashing process.

In a third step, as shown in FIG. 1 c, a field oxide layer 108 is formedof a USG (Undoped Silicate Glass) or HDP (High Density Plasma) material,to completely fill up the trenches t1, t2. Further, a flattening processsuch as a CMP (Chemical Mechanical Polishing) etc. for the field oxidelayer 108 and the nitride layer 104 is performed so that a nitride layerpattern 107 partially remains on the first and second active regions I,II, to thus form first and second device isolation layers 110, 112 forfilling the trenches t1, t2. The first device isolation layer 110 isdefined as a layer to isolate between the first and second activeregions and the field region, and the second device isolation layer 112is defined as a layer to isolate devices of each active region.

In a fourth step, as shown in FIG. 1 d, the remaining nitride layer 107is removed by a wet etching using H₃PO₄, and the pad oxide layer 102 isremoved by a wet etching using a diluted HF, to thus expose the surfaceof the first and second active regions I, II. Subsequently, a firstthermal oxide layer 114 of 300 Å for high voltage use is formed on thesurface exposed portion of the First and second active regions I, II.

In a fifth step, as shown in FIG. 1 e, a photoresist pattern 111 forexposing the first active region I and a portion of the first deviceisolation layer 110 is formed, and then, the first thermal oxide layeris etched by using the photoresist pattern 111 as an etch mask, toselectively leave the first thermal oxide layer 114 only on the secondactive region II.

In a sixth step, as shown in FIG. 1 f, the photoresist pattern 111 isremoved by an ashing process, and a second thermal oxide layer 116 of 40Å for use of low voltage is formed on the first active region I, to thuscomplete a dual gate oxide layer process. Of course, in forming thesecond thermal oxide layer 116, the first thermal oxide layer 114 alsogrows an insignificant amount.

As the result of that process, the thinned gate oxide layer 116 ofsecond thermal oxide material for use of a low voltage is formed on thefirst active region I, and the thick gate oxide layer 114 of firstthermal oxide material for use of a high voltage is formed on the secondactive region II.

Even though this structure of dual gate oxide layer based on the priorart can increase an integration of device, a size of active region has afixed structure, and an upper part of STI is positioned higher than anupper part of the active region, causing a stepped structure, thus thereare many problems as follows.

First, since the upper part of STI is positioned higher than an upperpart of the active region, i.e., the stepped structure, a trenchsidewall portion can not be used as the active region, which cause theactive region to have a fixed size.

Also, in a subsequent gate etching process, a stringer based on thestepped coverage between an active region and a field region is caused.

Further, the STI is formed of field oxide material such as USG or HDPetc., and the gate oxide layer is formed of thermal oxide material, thusin using an etching process to form the dual gate oxide layer, a severedent is caused on a boundary face between the active region and thefield region owing to a wet etching rate difference between the fieldoxide layer and the thermal oxide layer.

Embodiments of the invention address these and other limitations of theprior art.

SUMMARY OF THE PRESENT INVENTION

Example embodiments of the present invention provide a dual gate oxidestructure in a semiconductor device and a method of forming thestructure, which is capable of extending an area of active region byutilizing a trench sidewall portion of device isolation layer as theactive region. Herewith, a cell current of active region can increase toenhance a characteristic of device. In addition, a stringer causable bya stepped coverage between an active region and a field region can beprevented, and it can be prevented a dent causable on a boundary facebetween the active region and the field region owing to a wet etchingrate difference between field oxide material formed on a STI and thermaloxide material formed on the active region.

According to an exemplary embodiment of the present invention, a methodof forming a dual gate oxide layer includes, sequentially accumulating afirst insulation layer and a second insulation layer on a semiconductorsubstrate; sequentially etching the second insulation layer, the firstinsulation layer and a portion of the semiconductor substrate, andforming a trench for defining first and second active regions on thesemiconductor substrate; filling up the trench with a field oxide layer,and then, flattening the field oxide layer and the second insulationlayer so that the second insulation layer accumulated on the firstinsulation layer remains by a determined thickness, to thus form adevice isolation layer; removing the remaining second insulation layer,and etching the first insulation layer and the device isolation layer insuch a way that an uppermost part of the device isolation layer ispositioned below an upper surface of the first and second activeregions; forming a first thermal oxide layer for use of a gate oxidelayer on the first and second active regions; and removing the firstthermal oxide layer provided with the first active region, and then,forming a second thermal oxide layer for use of a gate oxide layer onthe first active region, the second thermal oxide layer having athickness thinner than the first thermal oxide layer.

The device isolation layer is formed so that an uppermost part of thedevice isolation layer is positioned below by a determined thicknessfrom an upper surface of the first and second active regions.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other features of exemplary embodiment of the presentinvention will become readily apparent from the description of theexemplary embodiments that follows, with reference to the attacheddrawings.

FIGS. 1 a to 1 f are diagrams illustrating a sequential process in adual gate oxide forming method according to the prior art.

FIGS. 2 a to 2 h are diagrams illustrating a sequential process in adual gate oxide forming method according to an exemplary embodiment ofthe present invention.

DETAILED DESCRIPTION OF EXEMPLARY EMBODIMENTS OF THE INVENTION

The present invention and example embodiments, thereof, are more fullydescribed below with reference to FIGS. 2 a through 2 h. This presentinvention may, however, be embodied in many different forms and shouldnot be construed as being limited to the example embodiments set forthherein. Rather, these example embodiments are provided so that thisdisclosure is thorough and complete, and conveys the concept of thepresent invention to those skilled in the art.

FIGS. 2 a to 2 h are diagrams illustrating a sequential process of dualgate oxide forming method according to an exemplary embodiment of thepresent invention. The process classified into eight steps forconvenience will be described as follows.

Reference character I indicates a low voltage (LV) region as a firstactive region on which a thinned gate oxide layer will be formed, andreference character II designates a high voltage (HV) region as a secondactive region on which a thick gate oxide layer will be formed. The HVregion indicates a region designed to have an internal voltage ofapproximately 3.3V through 50V in an operating voltage.

In a first step, as shown in FIG. 2 a, a first insulation layer 202 anda second insulation layer 204 are sequentially accumulated (205) on asemiconductor substrate 200. Next, on the second insulation layer 204, aphotoresist pattern 209 is formed for exposing a portion where a trenchfor defining a first active region I and a second active region II willbe formed, and a portion where a trench for a device isolation will beformed on each active region. Further, an oxide layer 206 of MTO (MediumTemperature Oxide) material formed at a temperature of approximately700° C. through 800° C. is additionally formed on the second insulationlayer 204, and the photoresist pattern 209 is desirably formed on thisMTO 206.

The first insulation layer 202 can be formed of oxide material through athermal oxide method, and the second insulation layer 204 can be formedthrough LPCVD (Low Pressure Chemical Vapor Deposition), for example.

Further, in performing a flattening process such as a chemicalmechanical polishing (CMP) etc., the second insulation layer 204 can beformed of SiN or SiON material having a relatively low removal rate ascompared with the field oxide layer.

In a second step, as shown in FIG. 2 b, the MTO 206, the secondinsulation layer 204, the first insulation layer 202 and thesemiconductor substrate 200 are sequentially etched by using thephotoresist pattern 209 as an etch mask, to form a trench t1 fordefining the first active region I and the second active region II onthe semiconductor substrate 200 and a trench t2 for isolating devices oneach active region. Then, a remaining photoresist pattern 209 is removedby, for instance, an ashing process.

In a third step, as shown in FIG. 2 c, the trenches t1, t2 are filledwith a field oxide layer 208, and then, the field oxide layer 208, theMTO 206 and the second insulation layer 204 are flattened through aflattening process such as the CMP etc. so that the second insulationlayer 204 accumulated on the first insulation layer 202 remains (207) ata determined thickness. This thus forms a first device isolation layer210 for defining the first active region I and the second active regionII and a second device isolation layer 212 for isolating devicesprovided on each active region. The first device isolation layer 210 isdefined to isolate the first and second active regions and the fieldregion, and the second device isolation layer 212 is defined to isolatedevices of each active region.

The field oxide layer 208 fills the trenches t1, t2 enough tosufficiently cover a surface of the semiconductor substrate. Further,the field oxide layer 208 may be formed of, for example, an oxide layergroup such as SOG (Spin On Glass), USG (Undoped Silicate Glass), BPSG(Boron Phosphorus Silicate Glass), PSG (Phosphor Silicate Glass),PE-TEOS (Plasma Enhanced Tetra Ethyl Ortho Silicate) and flowable oxidematerial, or can be formed of a multilayer containing two or more fromthe oxide layer group. The oxide layer group can be formed through a CVD(chemical vapor deposition), a reflow system and a deposition using ahigh density plasma (HDP) equipment, for example. In performing the CMP,the second insulation layer 204 functions as a stop layer on which thepolishing operation is ultimately stopped.

In a fourth step, as shown in FIG. 2 d, the remaining second insulationlayer 207 is removed by a wet etching using, for example, H₃PO₄.

Subsequently, the first insulation layer 202 and the device isolationlayers 210, 212 together are etched so that an uppermost part of thefirst and second device isolation layers 210, 212 is positioned below anupper surface of the first and second active regions I, II with adifference of determined thickness (h), resulting in FIG. 2 dillustrating that an upper surface of each active region I, II andsidewalls 215, 217 of less-filled trenches are exposed.

The first insulation layer 202 is formed of oxide material, and thefield oxide layer 208 constituting the device isolation layers 210, 212may also be formed of oxide material, thus the first insulation layer202 and the device isolation layers 210, 212 together can be etched bycontrolling etching equipment. That is, the device isolation layers 210,212 are made of the same material are etched at the same time when thefirst insulation layer 202 is etched. Thus the first insulation layer isremoved and an upper part of the device isolation layer 210, 212 can beformed so as to be positioned below by a determined thickness (h) froman upper surface of the first and second active regions I, II.Therefore, a process of specifically removing the first insulation layer202, which is required for the prior art, is unnecessary usingembodiments of the invention.

Further, an end of uppermost part of the device isolation layer 210, 212is positioned below by a determined thickness (h) from an upper surfaceof the first and second active regions I, II, thus surfaces ofless-filled trench sidewalls 215, 217 are exposed so that a gate oxidelayer can be formed in the exposed portions in a subsequent process.

The determined thickness (h) may have a significant meaning in thepresent invention in that the end of uppermost part of the deviceisolation layer 210, 212 is positioned below the upper surface of thefirst and second active regions I, II so as to increase an effectivearea of the active region by utilizing the surfaces 215, 217 of theless-filled trench sidewalls 215, 217 as the active region. Herewith, inconsidering possible defects in the device isolation, it is desirable toform the device isolation layer 210, 212 to be positioned below by about200 Å through 300 Å from the upper surface of the first and secondactive regions I, II.

In the prior art there was the problem for the stepped coverage that asidewall portion of trench can not be utilized as the active regionbecause the uppermost end of the device isolation layer was positionedhigher than an upper surface of the active region. However, inembodiments of the present invention, the end of uppermost part of thedevice isolation layer 210, 212 is positioned below the upper surface ofthe first and second active regions I, II, thus the less-filled trenchsidewalls 215, 217 can be used as the active region to increase an areaand cell current of the active region. Further, as was described above,even in forming the device isolation layer so that the uppermost end ofthe device isolation layer 210, 212 is positioned below the uppersurface of the first and second active regions I, II, the oxide layer ofthe first and second active regions I, II can be formed by a normalthickness on the less-filled trench sidewalls 215, 217 of the deviceisolation layer. In other words, the less-filled trench sidewalls 215,217 can be utilized as the active region.

If the field region is positioned higher than the active region such asin the prior art, a poly stringer can be caused in a subsequent gateetching process, but in embodiments of the present invention, thestringer can be prevented since the field region is positioned below theactive region.

It can be also prevented a phenomenon that a severe dent is caused on aboundary face between the active region and the field region due to awet etching rate difference between materials of the field oxide layerformed on the device isolation layer and of thermal oxide layer formedon the active region.

In a fifth step, as shown in FIG. 2 e, a first thermal oxide layer 214of about, for example, 400 through 450 Å for use in high voltageapplications is formed on the exposed surface of the first and secondactive regions I, II. Thus, the first thermal oxide layer 214 is alsoformed on the exposed portion of the less-filled trench sidewalls 215,217 by a normal thickness. That is, a first sidewall 215 of theless-filled trench can be utilized as the active region.

In a sixth step, as shown in FIG. 2 g, a photoresist pattern 211 forexposing the first active region I and a portion of the first deviceisolation layer 210 is formed, and then, the first thermal oxide layeris etched by using the photoresist pattern 211 as an etch mask, toselectively leave the first thermal oxide layer 214 only on the secondactive region II.

In a seventh step, as shown in FIG. 2 f, the photoresist pattern 211 isremoved by an ashing process, and a second thermal oxide layer 216 of 30through 50 Å for low voltage uses is formed on the first active regionI, to thus complete the dual gate oxide layer process. It goes withoutsaying that, the second thermal oxide layer 216 is formed by a normalthickness on an exposed portion of the second sidewall 217 provided withthe less-filled trench of the first active region, therefore, the secondsidewall 217 of the less-filled trench can be used as the active region.In forming the second thermal oxide layer 216, the first thermal oxidelayer 214 grows insignificantly.

As the result of these processes, an uppermost end of the deviceisolation layer 210, 212 is positioned below an upper surface of thefirst and second active regions I, II, and the thinned gate oxide layer216 of second thermal oxide material for use of low voltage is formed onan upper surface of the first active region I and on the second sidewall217 of less-filled trench, and the thick gate oxide layer 214 of firstthermal oxide material for high voltage use is formed on an uppersurface of the second active region II and on the first sidewall 215 ofthe less-filled trench.

According to this exemplary embodiment of the present invention, an endof uppermost part of the device isolation layer is positioned below anupper surface of the active region, thus the less-filled trench sidewallcan be used as the active region to increase an area and cell current ofthe active region. In addition, stringers caused by a stepped coveragebetween the active region and field region can be prevented. Furthersevere dents found in the prior art that are caused on a boundarybetween the active region and the field region, owing to a wet etchingrate difference between materials of the field oxide layer formed on theSTI and of the thermal oxide layer formed on the active region of theprior art can also be prevented.

In an eighth step, as shown in FIG. 2 h, a polysilicon layer 219 isaccumulated on the gate oxide layer that is formed on an upper surfaceof respective active regions I, II and on sidewalls of the less-filledtrenches t1, t2, thus gate patterns 218, 220 are each formed on thefirst and second active regions. The gate patterns 218, 220 are adaptedto use, not only an upper part of each active region but also sidewallsof the less-filled trenches t1, t2, as a channel region, therefore anarea of the channel region increases and a cell current increases.

The gate pattern is not limited to the designed scheme described in theexemplary embodiment of the present invention, but can be designedvariously.

In the meantime, a nitride layer masking method as an example can beapplied in conjunction with the present invention, instead of thegeneral photolithograph process described above in the inventiveexemplary embodiment.

Though was not shown in the drawings, the device isolation layer 210 isformed so that an uppermost part thereof is positioned below an uppersurface of the first and second active regions I, II, and thereon, anitride layer is deposited entirely. Subsequently, the nitride layer isselectively etched so as to expose the second active region II and aportion of the device isolation layer 210, to thus selectively leave thenitride layer only the first active region I. Then, the remainingnitride layer is used as a mask, to form the first thermal oxide layer214 of about 400 through 450 Å for use of high voltage on an exposedsurface of the second active region II, and next, the remaining nitridelayer is removed and the second thermal oxide layer 216 of 30 through 50Å for use of low voltage is formed on the first active region. Thereby,it is completed a process of forming the dual gate oxide layer that theuppermost part of device isolation layer is positioned below the uppersurface of the active region.

As was described above, according to an exemplary embodiment of thepresent invention, a trench interface of STI is utilized as an activeregion to increase an area of the active region with an effect ofincreasing a cell current.

Further, defects caused by an irregular thickness between the pad oxidelayer and the thermal oxide layer of high voltage region can be reduced,or eliminated, and a stringer caused by a stepped coverage between theactive region and the field region can be prevented.

In addition, it can be prevented a dent caused on a boundary facebetween the active region and the field region owing to a wet etchingrate difference between materials of the field oxide layer formed on theSTI and of the thermal oxide layer formed on the active region.

Of course, the invention can be practiced in a number of ways, and theparticular embodiments described above and below are only examples, andare not limited to their details.

According to further exemplary embodiments of the present invention, ina method of manufacturing a dual gate insulation layer of asemiconductor device which has first and second active regions operatingat mutually different voltages on a semiconductor substrate, the firstand second active regions having a device isolation layer of STI(Shallow Trench Isolation) structure; the method includes forming thedevice isolation layer so that an uppermost part of the device isolationlayer is positioned lower than an upper surface of the first and secondactive regions, before forming a gate insulation layer corresponding toeach of the first and second active regions.

To achieve the invention and according to an exemplary embodiment of thepresent invention, in a dual gate oxide structure of a semiconductordevice which has first and second active regions operating at mutuallydifferent voltages on a semiconductor substrate, the first and secondactive regions having a device isolation layer of STI structure; thestructure includes a device isolation layer whose uppermost part isformed lower than an upper surface of the first and second activeregions.

Herewith, an area of the active region increases to increase a cellcurrent, thus a characteristic of the device is enhanced, and a stringercaused by a stepped coverage between the active region and a fieldregion is prevented, and a dent caused on a boundary face between theactive region and the field region is prevented.

It will be apparent to those skilled in the art that modifications andvariations can be made in the present invention without deviating fromthe spirit or scope of the invention. Thus, it is intended that thepresent invention cover any such modifications and variations of thisinvention provided they come within the scope of the appended claims andtheir equivalents. Accordingly, these and other changes andmodifications are seen to be within the true spirit and scope of theinvention as defined by the appended claims.

1. A method of manufacturing a dual gate insulation layer of asemiconductor device which has first and second active regions operatingat mutually different voltages on a semiconductor substrate, said firstand second active regions having a device isolation layer of STI(Shallow Trench Isolation) structure, said method comprising: formingthe device isolation layer so that an uppermost part of the deviceisolation layer is positioned lower than an upper surface of the firstand second active regions, before forming a gate insulation layercorresponding to each of the first and second active regions.
 2. A dualgate oxide structure in a semiconductor device having first and secondactive regions operating at mutually different voltages and a deviceisolation layer of STI structure, said structure comprising: a deviceisolation layer for isolating between the first and second activeregions, isolating between respective transistor devices provided withthe first and second active regions, an upper surface of said deviceisolation layer being formed lower than an upper surface of the firstand second active regions; a first gate oxide layer formed on an uppersurface of the first active region and on an STI sidewall in which thedevice isolation layer within the first active region is partiallyfilled; and a second gate oxide layer formed on an upper surface of thesecond active region and on an STI sidewall in which the deviceisolation layer within the second active region is partially filled. 3.The dual gate oxide structure of claim 1, wherein the first activeregion is a low voltage region.
 4. The dual gate oxide structure ofclaim 1, wherein an uppermost part of the device isolation layer ispositioned below by about 200 Å through 300 Å from an upper surface ofthe first and second active regions.